| Tungsten carbide material specification | |||||
| Grade | Binder (Wt %)Cobalt | Density (g/cm3) | Hardness (HRA) | TRS (>N/mm²) | Grain Size(μm) |
| YG6 | 5.8-6.3 | 14.6-15.0 | 89.5-91 | 1800 | 0.8-2.0 |
| YG6X | 5.8-6.3 | 14.4-14.7 | 90.5-91.5 | 1650 | 0.6-1.0 |
| YG8 | 7.5-8.2 | 14.4-14.7 | 89.0-90.5 | 2200 | 1.0-1.5 |
| YG11 | 11.0-11.5 | 14.2-14.4 | 87.0-88.5 | 2800 | 1.0-2.0 |
| YG11C | 11.0-11.5 | 14.2-14.4 | 86.0-88.0 | 3000 | 1.0-2.5 |
| YG15 | 14.5-15 | 13.9-14.0 | 86.0-88.0 | 3300 | 1.0-2.0 |
| YG20 | 20.0-20.5 | 13.2-13.5 | 84.0-85.0 | 3400 | 1.0-2.0 |
| YG20C | 20.0-20.5 | 13.2-13.5 | 83.0-85.0 | 3600 | 1.0-2.5 |
| K05VF | 4.5-5.0 | 14.6-15.0 | 92.5-93.0 | 1500 | 0.6-1.0 |
| K10VF | 5.5-6.2 | 14.5-14.7 | 91.5-92.5 | 1550 | 0.6-1.0 |
| K20VF | 7.5-8.0 | 14.5-14.7 | 90.5-91.5 | 1800 | 0.6-1.0 |
| Grade | Binder (Wt %)Nickel | Density (g/cm3) | Hardness (HRA) | TRS (>N/mm²) | Grain Size(μm) |
| YN6 | 5.5-6.2 | 14.6-15.0 | 89.5-90.5 | 1800 | 0.8-2.0 |
| YN6X | 5.9-6.5 | 14.5-14.9 | 89.4-91 | 1750 | 0.8-1.8 |
| YN6A | 5.9-6.5 | 14.5-14.8 | 89.5-91.5 | 1850 | 0.8-1.8 |
| YN7 | 6.8-7.2 | 14.4-14.8 | 89.0-90.0 | 1900 | 0.8-1.6 |
| YN8 | 7.8-8.3 | 14.5-14.8 | 89.0-90.0 | 2200 | 0.8-2.0 |
| YN12 | 11.5-12.2 | 14.0-14.4 | 87.5-88.5 | 2600 | 0.8-2.0 |
| YN15 | 14.5-15.2 | 13.7-14.2 | 86.5-88.0 | 2800 | 0.6-1.5 |
Value:
Tungsten Carbide Bushing, as a wear-resistant component, is suitable for various machines that require long-term operation and plays an important role in the material field. This excellent wear resistance and corrosion resistance can ensure that the Carbide Bushing Tool can still maintain its working efficiency during use, making it the primary choice of many manufacturers.
Highlights:
1. Ultra-abrasion resistance
2. Exceeding hardness and toughness
3. Numerous levels can be chosen
4. Suitable price with extremely high quality
Advantages:
Tungsten Carbide Bush has low maintenance cost and good compressibility. As a wear-resistant part to be replaced, its service life is objective among many materials.