| Tungsten carbide material specification | |||||
| Grade | Binder (Wt %)Cobalt | Density (g/cm3) | Hardness (HRA) | TRS (>N/mm²) | Grain Size(μm) |
| YG6 | 5.8-6.3 | 14.6-15.0 | 89.5-91 | 1800 | 0.8-2.0 |
| YG6X | 5.8-6.3 | 14.4-14.7 | 90.5-91.5 | 1650 | 0.6-1.0 |
| YG8 | 7.5-8.2 | 14.4-14.7 | 89.0-90.5 | 2200 | 1.0-1.5 |
| YG11 | 11.0-11.5 | 14.2-14.4 | 87.0-88.5 | 2800 | 1.0-2.0 |
| YG11C | 11.0-11.5 | 14.2-14.4 | 86.0-88.0 | 3000 | 1.0-2.5 |
| YG15 | 14.5-15 | 13.9-14.0 | 86.0-88.0 | 3300 | 1.0-2.0 |
| YG20 | 20.0-20.5 | 13.2-13.5 | 84.0-85.0 | 3400 | 1.0-2.0 |
| YG20C | 20.0-20.5 | 13.2-13.5 | 83.0-85.0 | 3600 | 1.0-2.5 |
| K05VF | 4.5-5.0 | 14.6-15.0 | 92.5-93.0 | 1500 | 0.6-1.0 |
| K10VF | 5.5-6.2 | 14.5-14.7 | 91.5-92.5 | 1550 | 0.6-1.0 |
| K20VF | 7.5-8.0 | 14.5-14.7 | 90.5-91.5 | 1800 | 0.6-1.0 |
| Grade | Binder (Wt %)Nickel | Density (g/cm3) | Hardness (HRA) | TRS (>N/mm²) | Grain Size(μm) |
| YN6 | 5.5-6.2 | 14.6-15.0 | 89.5-90.5 | 1800 | 0.8-2.0 |
| YN6X | 5.9-6.5 | 14.5-14.9 | 89.4-91 | 1750 | 0.8-1.8 |
| YN6A | 5.9-6.5 | 14.5-14.8 | 89.5-91.5 | 1850 | 0.8-1.8 |
| YN7 | 6.8-7.2 | 14.4-14.8 | 89.0-90.0 | 1900 | 0.8-1.6 |
| YN8 | 7.8-8.3 | 14.5-14.8 | 89.0-90.0 | 2200 | 0.8-2.0 |
| YN12 | 11.5-12.2 | 14.0-14.4 | 87.5-88.5 | 2600 | 0.8-2.0 |
| YN15 | 14.5-15.2 | 13.7-14.2 | 86.5-88.0 | 2800 | 0.6-1.5 |
Value:
Machined Bushings play an important function in numerous mechanical tools. However, due to their tiny dimension, they are commonly ignored. In the manufacturing procedure of a solitary auto, almost one hundred Machining Bushings are utilized. When the shaft revolves, Bushing Sleeve lies in between the shaft and various other parts, contributing to decreasing friction.
Highlights:
1. Superior abrasion resistance as a wear part
2. Extremely long using lifespan
3. Extraordinary heat working tolerance
4. Easy to be customized in accordance with the requirements
Advantages:
The manufacturing and handling procedures of the Carbide Bushing Tool are incredibly accurate, and also the fragment dimension and structure proportion of tungsten need to be purely managed from the start of product choice.