| Tungsten carbide material specification | |||||
| Grade | Binder (Wt %)Cobalt | Density (g/cm3) | Hardness (HRA) | TRS (>N/mm²) | Grain Size(μm) |
| YG6 | 5.8-6.3 | 14.6-15.0 | 89.5-91 | 1800 | 0.8-2.0 |
| YG6X | 5.8-6.3 | 14.4-14.7 | 90.5-91.5 | 1650 | 0.6-1.0 |
| YG8 | 7.5-8.2 | 14.4-14.7 | 89.0-90.5 | 2200 | 1.0-1.5 |
| YG11 | 11.0-11.5 | 14.2-14.4 | 87.0-88.5 | 2800 | 1.0-2.0 |
| YG11C | 11.0-11.5 | 14.2-14.4 | 86.0-88.0 | 3000 | 1.0-2.5 |
| YG15 | 14.5-15 | 13.9-14.0 | 86.0-88.0 | 3300 | 1.0-2.0 |
| YG20 | 20.0-20.5 | 13.2-13.5 | 84.0-85.0 | 3400 | 1.0-2.0 |
| YG20C | 20.0-20.5 | 13.2-13.5 | 83.0-85.0 | 3600 | 1.0-2.5 |
| K05VF | 4.5-5.0 | 14.6-15.0 | 92.5-93.0 | 1500 | 0.6-1.0 |
| K10VF | 5.5-6.2 | 14.5-14.7 | 91.5-92.5 | 1550 | 0.6-1.0 |
| K20VF | 7.5-8.0 | 14.5-14.7 | 90.5-91.5 | 1800 | 0.6-1.0 |
| Grade | Binder (Wt %)Nickel | Density (g/cm3) | Hardness (HRA) | TRS (>N/mm²) | Grain Size(μm) |
| YN6 | 5.5-6.2 | 14.6-15.0 | 89.5-90.5 | 1800 | 0.8-2.0 |
| YN6X | 5.9-6.5 | 14.5-14.9 | 89.4-91 | 1750 | 0.8-1.8 |
| YN6A | 5.9-6.5 | 14.5-14.8 | 89.5-91.5 | 1850 | 0.8-1.8 |
| YN7 | 6.8-7.2 | 14.4-14.8 | 89.0-90.0 | 1900 | 0.8-1.6 |
| YN8 | 7.8-8.3 | 14.5-14.8 | 89.0-90.0 | 2200 | 0.8-2.0 |
| YN12 | 11.5-12.2 | 14.0-14.4 | 87.5-88.5 | 2600 | 0.8-2.0 |
| YN15 | 14.5-15.2 | 13.7-14.2 | 86.5-88.0 | 2800 | 0.6-1.5 |
Value:
Among the largest features of the Machined Bushings is to deal with the placement and to avoid the mechanical tools from changing in some instructions as a result of running resonance. Furthermore, the Machining Bushings will additionally be utilized as a safety device to cover the beyond the shaft. Occasionally the shaft facility requires to revolve at broadband under heat and high pressure. If there is no Bushing Sleeve, the life span of the shaft facility will be much shorter.
Highlights:
1. Enhanced strength and toughness
2. Super raw material quality
3. Outstanding temperature resistance
4. Super customized service
Advantages:
The chemical residential property of tungsten carbide is secure, and it will not flaw even in a severe atmosphere. What's more its structure will not respond with the adjustment of atmosphere.